3920621985 - Three-layer transparent plastic film consisting of a 15 µm fluorinated polymer (FCC) (EVA) layer, a 275 µm polyethylene terephthalate (PET) layer and a 25 µm fluorinated polymer (FCC) layer with:
-a total thickness of 300 µm or more, but not more than 330 µm,
-a tensile strength of 375 N/cm or more in both the longitudinal and transverse directions (ASTM D-882),
-a low thermal shrinkage of 1 % or less at 150 °C for 30 minutes,
-a low water vapor permeability of 2,5 g/m²•d or less, and
-a high breakdown voltage of 18 kV or more and
-a partial discharge voltage of 1500 VDC or more (BG/T 123542.2-2009)
to be used as a protective layer on the back of photovoltaic modules
Definition & language versions
Three-layer transparent plastic film consisting of a 15 µm fluorinated polymer (FCC) (EVA) layer, a 275 µm polyethylene terephthalate (PET) layer and a 25 µm fluorinated polymer (FCC) layer with:
-a total thickness of 300 µm or more, but not more than 330 µm,
-a tensile strength of 375 N/cm or more in both the longitudinal and transverse directions (ASTM D-882),
-a low thermal shrinkage of 1 % or less at 150 °C for 30 minutes,
-a low water vapor permeability of 2,5 g/m²•d or less, and
-a high breakdown voltage of 18 kV or more and
-a partial discharge voltage of 1500 VDC or more (BG/T 123542.2-2009)
to be used as a protective layer on the back of photovoltaic modules
Tip: confirm material, use and finished-product form first, then compare hierarchy and declarable candidates below.
ZH
三层透明塑料薄膜,由15微米氟化聚合物（FCC）（EVA）层、275微米聚对苯二甲酸乙二酯（PET）层和25微米氟化聚合物（FCC）层组成,总厚度300至330微米,拉伸强度≥375N/cm（ASTM D-882）,150°C热收缩率≤1%（30分钟）,水蒸气透过率≤2.5g/m²·d,击穿电压≥18kV,局部放电电压≥1500VDC（BG/T 123542.2-2009）,用于光伏组件背板保护层
DE
Dreilagige transparente Kunststofffolie, bestehend aus einer 15 µm dicken Schicht aus fluoriertem Polymer (FCC) (EVA), einer 275 μm dicken Schicht aus Polyethylenterephthalat (PET) und einer 25 μm dicken Schicht aus fluoriertem Polymer (FCC) mit
-einer Gesamtdicke von 300 μm oder mehr, jedoch nicht mehr als 330 μm
-einer Zugfestigkeit von 375 N/cm oder mehr in Längs- und Querrichtung (ASTM D-882)
-einer geringen thermischen Schrumpfung von 1 % oder weniger bei 150 °C für 30 Minuten
-einer geringen Wasserdampfdurchlässigkeit von 2,5 g/m²•d oder weniger
-einer hohen Durchschlagsspannung von 18 kV oder mehr und
-einer Teilentladungsspannung von 1 500 VDC oder mehr (BG/T 123542.2-2009)
zur Verwendung als Schutzschicht auf der Rückseite von Photovoltaikmodulen
EN
Three-layer transparent plastic film consisting of a 15 µm fluorinated polymer (FCC) (EVA) layer, a 275 µm polyethylene terephthalate (PET) layer and a 25 µm fluorinated polymer (FCC) layer with:
-a total thickness of 300 µm or more, but not more than 330 µm,
-a tensile strength of 375 N/cm or more in both the longitudinal and transverse directions (ASTM D-882),
-a low thermal shrinkage of 1 % or less at 150 °C for 30 minutes,
-a low water vapor permeability of 2,5 g/m²•d or less, and
-a high breakdown voltage of 18 kV or more and
-a partial discharge voltage of 1500 VDC or more (BG/T 123542.2-2009)
to be used as a protective layer on the back of photovoltaic modules
Classification hints
This code appears to be a directly declarable leaf candidate and can be used for the next customs-filing step.
Please check validity dates and duty effective dates, as the applicable rule may depend on the filing date.
Codes
TARIC
39206219 85
CN (8 digits)
39206219
HS (6 digits)
392062
Updated at
Mon Aug 31
Duty
Duty rate (import)
0.000%
Effective from
Thu Jan 01
Legal base
Regulation 2605/25
Validity & quantity
Start date
Tue Jul 01
End date
-
Supplementary unit
Not required
Code hierarchy
TARIC
Trade measures and restrictions
This block shows a filing-oriented summary first, then imported TARIC measures including scope, add. codes, order numbers, duty expressions and legal bases.
Measure
Current value
Notes / validity
Reference import duty
0.000%
Effective from Thu Jan 01
Legal base
Regulation 2605/25
-
Supplementary unit
Not required
Validity: Tue Jul 01 - -
Imported TARIC measures
No detailed TARIC measures are available for this code in the current import yet. Use the summary above and verify against the official TARIC page.
Siblings
3920621905
Poly(ethylene terephthalate) film in rolls:
-|with a thickness of 0,335|mm or more but not more than 0,365|mm, and
-|coated with a gold layer with a|thickness of 0,03|μm or more but not more than 0,06|μm
3920621908
Poly(ethylene terephthalate) film, not coated with an adhesive, of a thickness of not more than 25|µm, either:
-|only dyed in the mass, or
-|dyed in the mass and metallised on one side
3920621928
Non-transparent poly(ethylene terephthalate) film:
-each outer layer with a thickness of 7 nm or more but not more than 80 nm,
-with a tensile strength of 300 N/cm or more (ASTM D-882),
-with a total thickness of 200 µm or more but not more than 350 µm, and
-with a width of 600 mm or more but not more than 1 600 mm
- covered on one side with a layer of a fluoropolymer, and on the other side with an adhesive and a layer of polyvinylidene difluoride, or coated on both sides with polyvinylidene difluoride or polyvinyl fluoride based on fluorinated polymer composites
3920621932
Transparent poly(ethylene terephthalate) film:
-having thickness of both sides of 7 nm or more but not more than 80 nm, or thickness of both sides of 7 µm or more but not more than 80 µm, whether coated with an acrylic-based organic material or not,
-with a surface tension of 36 Dyne/cm or more but not more than 39 Dyne/cm, or transparent 3 or 4 layers, second layer of PET, and other layers contain fluorine resin,
-with a light transmittance of more than 70 %,
-with a haze value of not more than 1,3 %,
-with a total thickness of 10 µm or more but not more than 350 µm,
-with a width of 800 mm or more but not more than 1 600 mm
3920621938
Poly(ethylene terephthalate) film, of a thickness of not more than 12|µm, coated on one side with a layer of aluminium oxide of a thickness of not more than 35|nm
3920621948
Sheets or rolls of poly(ethylene terephthalate):
-|coated on both sides with a layer of epoxy acrylic resin,
-|of a total thickness of 37|μm (±|3|μm)
3920621952
Film of poly(ethylene terephthalate), poly(ethylene naphthalate) or similar polyester, coated on one side with metal and/or metal oxides, containing by weight less than 0,1|% of aluminium, of a thickness of not more than 300|µm and having a surface resistivity of not more than 10|000|ohms (per square) (as determined by the ASTM D 257|method)
3920621960
Poly (ethylene terephtalate) film:
-|of a thickness of not more than 20|µm,
-|coated on at least one side with a gas barrier layer consisting of a polymeric matrix in which silica or aluminium oxide has been dispersed and of a thickness of not more than 2µm
3920621979
Reflective film of polyethylene terephthalate, embossed in a pyramidal pattern, with
-a thickness of 0.07 mm or more but not more than 0.15 mm
-a width of 762 mm or more but not more than 1350 mm
3920621999
Other
This page provides public lookup and helper information only and is not customs/tax/legal advice. Official TARIC/EZT sources prevail.
TARIC change hints
After a monthly TARIC update, this block shows a hint about text changes versus the previous snapshot.
Source: internal TARIC diff (hint only)
Previous
No previous text
→
Current
Dreilagige transparente Kunststofffolie, bestehend aus einer 15 µm dicken Schicht aus fluoriertem Polymer (FCC) (EVA), e
Type: newSource lang: EN+DE
Next actions
If this code looks suitable for your product, continue with shipment creation or customs-entry forms.